C | SI | Mn | Cr | Mo | Nb | W | other |
Hardness |
DIN 8555 | Welding Process | |||||||
Product | % | % | % | % | % | % | % | % | O | G | SA | ||||||
Abrasion wear resistant wire | |||||||||||||||||
LZ570 | 4.3 | 0.7 | 0.6 | 21.0 | - |
- |
- |
55-61HRC | MF 10-55-G | √ | |||||||
LZ590 | 4.5 | 0.6 | 0.8 | 21.0 | - |
- |
- |
55-63HRC | MF 10-60-G | √ | |||||||
LZ601 | 4.5 | 1.0 | 1.0 | 26.0 | - |
- |
- |
55-63HRC | MF 10-60-G | √ | |||||||
LZ602 | 4.6 | 1.0 | 1.0 | 21.0 | - |
7.0 |
- |
55-63HRC | MF 10-60-G | √ | |||||||
LZ603 | 4.8 | 1.0 | 1.0 | 29.0 | - |
- |
- |
55-63HRC | MF 10-60-G | √ | |||||||
LZ606 | 5.0 | 1.0 | 2.0 | 26.0 | 1.2 |
- |
- |
55-62HRC | MF 10-60-G | √ | |||||||
LZ632 | 4.8 | 1.0 | 1.2 | 25.0 | 4.0 |
7.0 |
1.5 |
V:1.5 |
58-65HRC | MF 10-60-G | √ | ||||||
LZ642 | 5.0 | 0.9 | 1.0 | 29.0 | 2.0 |
- |
1.5 |
V:1.5 |
58-63HRC | √ | √ | ||||||
LZ643 | 5.4 | 0.9 | 0.6 | 21.0 | 1.0 |
1.0 |
1.0 |
59-65HRC | MF 10-65-G | √ | √ | ||||||
LZ650 | 5.5 | 0.6 | 0.8 | 26.0 | - |
- |
- |
58-65HRC | MF 10-65-G | √ | |||||||
LQ582 | 0.5 | 0.8 | 1.5 | 6.0 | 0.6 |
- |
0.6 |
V:0.3 |
55-60HRC | MF 6-60-RP | √ | ||||||
LQ586 | 0.5 | 0.8 | 1.2 | 9.0 | - |
- |
- |
55-60HRC | MF 6-55-RP | √ | |||||||
LQ605 | 4.3 | 0.8 | 0.9 | 25.0 | - |
- |
- |
55-61HRC | MF 10-55-G | √ | √ | ||||||
LQ707 | 3.0 | 1.0 | 1.0 | - | - |
- |
39.0 |
60-65HRC | √ | ||||||||
Metal to metal wear resistant wire | |||||||||||||||||
LQ337 | 0.4 | 1.0 | 1.0 | 4.5 | - |
- |
8.0 |
55-61HRC | MF 6-55-G | √ | |||||||
LZ414N | 45-52HRC | Contact us for more info. | √ | ||||||||||||||
LZ50-LC | 2.3 | 1.0 | 1.2 | 11.0 | 0.5 |
- |
- |
47-56HRC | MF 7-55-GP | √ | |||||||
LM414 | 0.06 | 1.0 | 1.0 | 13.0 | 1.0 |
- |
- |
Ni:4.0 |
40-50 HRC | MF 5-45-PRT | √ | ||||||
LM430 | 0.1 | 1.0 | 1.0 | 17.0 | - |
- |
- |
<30HRC | √ | ||||||||
LM491 | 0.3 | 0.9 | 1.0 | 9.0 | - |
- |
- |
53-59HRC | MF 6-50-P | √ | |||||||
LM551 | 0.4 | 0.9 | 1.5 | 3.5 | - |
- |
- |
53-59HRC | MF 10-55-PT | √ | |||||||
LM552 | 0.4 | 1.0 | 0.6 | 9.0 | - |
- |
- |
Ni:4.0 |
54-60HRC | MF 6-55-PT | √ | ||||||
Impact resistant wire | |||||||||||||||||
LZ100-TIC | 2.0 | 0.8 | 1.5 | 7.0 | 2.0 |
- |
- |
Ti:5.0 |
53-58 HRC | MF 7-55-GP | √ | ||||||
Work harden manganese wire | |||||||||||||||||
LQ257 | 1.0 | 0.4 | 14 | 4.0 | - |
- |
- |
>200HB | MF 7-200-KNP | √ | √ | ||||||
LQ276 | 0.2 | 1.0 | 15.0 | 14.0 | 0.2 |
- |
- |
>250HB | MF 7-250-KNP | √ | √ |