Gas Shielding 410NiMo Hardfacing flux cored wire LQ439
views:46484
Gas Shielded Hardfacing Flux Cored Wire LQ439
CLASSIFICATION:
EN14700 DIN 8555
T Fe 7 MF 5-45-RPT
CHARACTERISTICS:
Ø Material: Stainless steel 0Cr13Ni4Mo.
Ø Shielding gas: CO2(purity above 99.5%).
Ø Hardfacing deposit metal property: Excellent impact resistance& high-temperature oxidation resistance, suitable to metal-to-metal wear resistance, dust& slight abrasion resistance.
Ø Weldability: Stable welding arc, little spatter, excellent slag removal &perfect welding appearance.
Ø Suitable parent material:45# steel(ASTM 1045,JIS S45C, DIN C45) or similar steel.
Ø Hardfacing thickness limit: No limit.
Ø Crack resistance: Perfect. Likewise depends on parent material, workpiece size, hardfacing thickness, welding process, etc.
Ø Machining: Turning, milling,
Ø Diameter&Package:φ1.6mm, 15Kg/Spool.
APPLICATION:
LQ439 is a stainless steel hard surfacing cored wire, suitable for hard surfacing continuous casting rolls and alloy steel axles piston etc.
All Weld
Metal Chemical Composition (%) and Hardness
|
C |
Mn |
Si |
Cr |
Ni |
Mo |
Others |
Hardness |
|
0.1 |
<2.0 |
<1.5 |
13.5 |
4.0 |
1.2 |
<2.0 |
HRC40-50 |
Welding position: PA&PC.
PARAMETER:
|
Diameter(mm) |
Amperage(A) |
Voltage(V) |
Stickout(mm) |
Welding speed (mm/min) |
Preheat(℃) |
|
Φ1.6 |
220~320 |
25~32 |
20~30 |
300~400 |
200~300 |
² φ1.6mm:deposit efficiency: 91%.
² φ1.6mm: deposit efficiency: 5kg/hour.
Notes:
1. Remove fatigue layer, slag, oil and rust before welding.
2. Welding crack may occur , not damage the wear resistance ability. Preheating and slow cooling can reduce the risk. Recommended preheating temperature ≥200℃.
3. Stored in cool and dry place, use up within three days once opened.
Remark:
Chemical composition and hardness are tested according to prescribed standard,
actual results might be vary depending on many factors, like weld procedure,
temperature etc, please contact our sales before use it in the intended
application